Other grades of this product :
| TYLOXAPOL Basic information |
| Product Name: | TYLOXAPOL | | Synonyms: | ETHOXYLATED P-TERT-OCTYLPHENOL FORMALDEHYDE POLYMER;4-(1,1,3,3-TETRAMETHYLBUTYL)PHENOL POLYMER WITH FORMALDEHYDE AND OXIRANE;TYLOXAPOL;TRITON(R) WR-1339;4-(1,1,3,3-tetramethylbutyl)-phenopolymerwithformaldehydeandoxirane;alevaire;formaldehyde,polymerwithoxiraneand4-(1,1,3,3-tetramethylbutyl)phenol;macrocyclon | | CAS: | 25301-02-4 | | MF: | C17H28O3 | | MW: | 280.41 | | EINECS: | | Product Categories: | Polymers;Benzene derivatives | | Mol File: | 25301-02-4.mol |
| TYLOXAPOL Chemical Properties |
| density | 1.1 | | Fp | 113 °C | | storage temp. | under inert gas (nitrogen or Argon) at 2–8 °C | | solubility | Chloroform (Slightly), DMSO (Slightly), Methanol (Slightly) | | form | Viscous Liquid | | color | Clear to hazy yellow to amber | | Merck | 13,9901 | | CAS DataBase Reference | 25301-02-4(CAS DataBase Reference) |
| Hazard Codes | Xi | | Risk Statements | 36/37/38 | | Safety Statements | 26-36 | | WGK Germany | 2 | | RTECS | SM9750000 | | HS Code | 29222990 |
| TYLOXAPOL Usage And Synthesis |
| Chemical Properties | clear to hazy yellow to amber viscous liquid | | Originator | Solacen | | Uses | anthelmintic, hepatotoxic | | Uses | Tyloxapol, is a nonionic liquid polymer of the alkyl aryl polyether alcohol type. It is used as a surfactant to aid liquefaction and removal of mucopurulent (containing mucus and pus) bronchopulmonary secretions. Tyloxapol also blocks plasma lipolytic activity. | | Manufacturing Process | Srep 1: Into a 3-necked flask equipped with thermometer, mechanical
agitator, and reflux condenser was charged the following: 412 g of α,α,γ,γ-
tetramethylbutylphenol, 162 g of a 37% aqueous solution of formaldehyde,
and 27.6 g of water. The mixture was agitated and heated to a temperature of
90°C. At this point, 246 g of oxalic acid and 0.92 g of Twitchell's reagent
dissolved in 10 g of water were added. While being agitated, the reaction
mixture was refluxed for 6 hours. 200 g of water and 384 g of toluene were
added, and refluxing was continued for an hour.
Agitation was stopped and the contents of the flask were removed to a
separatory funnel. The aqueous and resinous layers were separated and the
solvent was removed from the resinous layer by vacuum distillation. After the
removal of the solvent, heating at a reduced pressure of 1.5 to 2.5 mm and at
a temperature of 245° to 250°C was continued for 4 1/2 hours. The
condensate then had a viscosity of 4.0 poises when measured as a 60%
solution in toluene and, on cooling, solidified to a brittle mass.
Step 2: A mixture of 118 parts of the product of Step 1, having hydroxyl
number of 260, 2 parts of solid NaH, and 100 parts of toluene was heated to
125° to 150°C in an autoclave. Ethylene oxide was added slowly over a period
of 2 1/2 hours until 261 parts of ethylene oxide were absorbed. This
corresponds to 11 mols of ethylene oxide per mol of phenol in the product of
Step 1. The toluene was then removed by steam distillation and the water by
vacuum distillation at 10°C. The product was obtained as a viscous paste
having a corrected hydroxyl number of 97. It was readily soluble in water and
had marked detergent properties. | | Brand name | Superinone (Sterling Winthrop). | | Therapeutic Function | Bronchodilator | | General Description | Tyloxapol is a biocompatible surfactant |
| TYLOXAPOL Preparation Products And Raw materials |
|